1. Zavedenie
CF3 stainless steel, a member of the austenitic cast stainless steel family, is the low-carbon cast equivalent of the popular wrought grade 304L (US S30403).
It is defined under ASTM A351 and widely used in industries where corrosion resistance, zvárateľnosť, and castability are paramount.
Ten “C” in CF3 stands for “Corrosion-resistant”, “F” denotes the steel grade (304L ekvivalent), and the number “3” identifies its low carbon content (≤ 0.03%).
Historicky, CF3 emerged as part of the response to corrosion issues in chloride-rich and welding-intensive applications.
The introduction of low-carbon grades in the mid-20th century was a milestone that enabled the development of high-integrity welded structures without the need for post-weld heat treatment.
Due to its balanced combination of cost-effectiveness, výkonnosť, and resistance to sensitization,
CF3 continues to be strategically important in cast stainless steel applications across chemical, petrochemický, úpravy vody, and food-processing sectors.
2. Chemické zloženie & Hutníctvo
Nominálne chemické zloženie
The typical weight percentage (wt.%) of the alloying elements in CF3 stainless steel, as defined by ASTM A351, je:
| Prvok | Typický rozsah (wt.%) | Funkcia |
|---|---|---|
| Chróm (Cr) | 18.0 - 21.0% | Promotes corrosion resistance through passive film formation |
| Nikel (V) | 8.0 - 11.0% | Stabilizuje austenit, Zlepšuje ťažnosť a tvrdosť |
| Uhlík (C) | ≤ 0.03% | Reduces sensitization; improves weldability |
| Mangán (Mn) | ≤ 1.5% | Enhances hot workability; deoxidizér |
| Kremík (A) | ≤ 2.0% | Podporuje plynulosť pri odliatení; deoxidizér |
| Fosfor (P) | ≤ 0.04% | Zvyškový; must be minimized to reduce brittleness |
| Síra (Siež) | ≤ 0.04% | Zvyškový; excessive S can reduce toughness |
| Žehlička (FE) | Vyvážiť | Maticový prvok |
Ten obsah s nízkym obsahom uhlíka (≤ 0.03%) significantly mitigates the risk of chromium carbide precipitation at grain boundaries during welding,
making CF3 especially resistant to intergranular corrosion without requiring post-weld heat treatment.
Mikroštruktúra: Austenitická matica & Carbide Control
CF3 stainless steel has a fully austenitická mikroštruktúra with a face-centered cubic (Fcc) mriežka, which contributes to:
- Excellent toughness at both ambient and cryogenic temperatures.
- Non-magnetic behavior v žíhanom stave.
- Resistance to stress corrosion cracking (Scc) in many chloride-containing environments.
Due to its low carbon content, CF3 contains minimal chromium carbides, particularly at grain boundaries.
This improves resistance to sensitization, a condition in which chromium-depleted zones form and become vulnerable to corrosive attack.
Some residual delta ferrite (zvyčajne < 10%) may be present after solidification, particularly in sand-cast components.
which helps prevent hot cracking during solidification, but has minimal impact on corrosion resistance or toughness when kept at controlled levels.
3. ASTM A351 CF3 and Global Equivalents
| Norma | Označenie | Región | Equivalent Grade |
|---|---|---|---|
| ASTM A351 | Grade CF3 | USA | Low-carbon cast 304L |
| ASME SA-351 | Grade CF3 | USA (boiler code) | Pressure vessel compliant |
| V 10283 | Gx2crni19-11 | European Union | Obsadený verzia 1.4306 (304L) |
| ISO 11972 | G-X2CrNi19-11 | Medzinárodný | Global harmonized equivalent |
| On G5121 | SCS13A | Japonsko | 304L cast grade |
4. Mechanické vlastnosti
| Mechanická vlastnosť | Typická hodnota |
|---|---|
| Pevnosť v ťahu | ≥ 485 MPa |
| Výnosová sila (0.2% kompenzácia) | ≥ 205 MPa |
| Predĺženie | ≥ 30% |
| Tvrdosť | 140–190 HB |
| Húževnatosť (Teplota miestnosti) | > 100 J (Charpy) |
| Fatigue Endurance Limit | 240–270 MPA (in air, leštený) |
| Odpor | Moderate up to 870°C |
Pri zvýšených teplotách, tensile and yield strengths decrease gradually, but the alloy retains sufficient structural integrity up to 400–500 °C, making it viable for moderate thermal service.
5. Tepelný & Fyzické vlastnosti
| Majetok | Hodnota |
|---|---|
| Hustota | ~ 7,9 g/cm³ |
| Tepelná vodivosť | ~ 16 w/m · k (pri 100 ° C) |
| Koeficient rozširovania | 17.3 µm/m · ° C (20–400 ° C) |
| Elektrický odpor | 0.72 µω · m |
| Magnetická reakcia | Nemagnetický (žíhaný) |
| Oxidácia | Good up to ~800°C |
6. Casting Characteristics of CF3 Stainless Steel
CF3 stainless steel—cast equivalent of 316—brings molybdenum‑enhanced corrosion resistance into complex geometries.
To harness its full potential, foundries must account for its unique casting behavior, from melt handling to solidification control.
Plynulosť & Nalievanie teploty
CF3 melts between 1450 ° C a 1550 ° C, slightly higher than CF8 due to its Mo content.
At a pouring superheat of 1500–1560 °C, CF3 achieves a fluidity of 220–280 mm (ISO 243), enabling fill of thin‑walled sections down to 4 mm.
Avšak, excessive superheat can increase gas pickup a oxidácia, so operators typically limit superheat to 50 ° C tekutý.
Solidification Range & Zhoršenie
S a mrazivý rozsah približne 60–90 °C, CF3 solidifies over a broader temperature interval than simple austenitic alloys.
Následne, it exhibits lineárne zmršťovanie z 1.9–2.3 %, necessitating careful shrink‑compensation in pattern design.
Predchádzať pórovitosť, engineers employ smerová tuhosť: placing insulated risers above hot spots and using chladenie to accelerate freezing in thick sections.
Feeding & Riser Design
Given its moderate shrinkage, CF3 castings benefit from risers sized to feed 30–40 % of the casting mass they support.
Finite‑element thermal simulation often guides riser placement, ensuring uninterrupted metal flow into contracting zones.
Navyše, exotermické rukávy on critical risers prolong feeding life without increasing overall mold volume.
Odpustenie, Deoxidation & Očkovanie
To minimize gas porosity, foundries typically argon‑purge the molten CF3 before pouring.
They also add kremík (0.3–0.6 %) a hliník (0.02–0.05 %) deoxidizers, which form stable oxides and reduce dissolved oxygen.
Konečne, a small rare‑earth inoculant (Napr., 0.03–0.05 % Fe‑Ce) promotes fine, uniform δ‑ferrite and prevents microshrinkage, enhancing mechanical consistency.
Suitable Casting Methods for CF3 Stainless Steel
| Metóda obsadenia | Typické aplikácie | Výhody | Úvahy |
|---|---|---|---|
| Odlievanie piesku (Green or No-Bake) | Telá ventilu, čerpacie puzdrá, príruba | – Cost-effective for large parts – Flexible for varied designs |
– Rougher surface finish (Ra 6–12 μm) – Tighter control needed for porosity |
| Odlievanie škrupín | Instrumentation covers, small valves | – Good dimensional accuracy (±0.3%) – Fine surface finish (Ra 3–6 μm) |
– More expensive molds – Best for small to medium-sized parts |
| Investičný casting (Stratený vosk) | Obaly, lekárske vybavenie, komponenty | – Excellent surface finish (Rana < 3 μm) – High geometric complexity |
– Higher cost – Limited to small–medium parts |
| Odstredivé odlievanie | Puzdro, prstene, úseky | – High density – Low porosity – Good mechanical properties in radial direction |
– Suitable only for rotationally symmetric parts |
| Vákuové liatie | Critical components in aerospace, nuclear applications | – Reduced oxidation – Cleaner microstructure |
– Expensive – Requires specialized equipment |
| Keramická pleseň | Complex heat-resistant parts | – Excellent surface detail – Good dimensional precision |
– Longer mold preparation time – Higher cost |
Heat Treatment Practices
Po obsadení, CF3 typically undergoes žíhanie riešenia v rozsahu 1040–1120 ° C (1900–2050°F) followed by rapid water quenching. This process serves several purposes:
- Dissolves residual carbides, restoring corrosion resistance
- Homogenizes the microstructure, eliminating segregation from solidification
- Improves ductility and toughness by removing delta ferrite or brittle phases
Strict temperature control during annealing is critical. Insufficient quenching rates can result in senzibilizácia a vyčerpanie chrómu na hraniciach zrna, ohrozenie odolnosti proti korózii.
7. Odpor
Všeobecná korózia
In neutral and mildly acidic environments, CF3 maintains excellent resistance due to its chromium-rich passive film. Corrosion rates are typically < 0.05 mm/year in potable water and wastewater systems.
Localized Corrosion Resistance
The alloy shows good performance in environments containing chlorides up to ~200 ppm:
- Číslo ekvivalentného odporu. (Drevo): ~ 18
- Critical Pitting Temperature (Cpt): ~ 20–25 ° C (varies with chloride level)
Praskanie korózie (Scc)
CF3’s low carbon content improves SCC resistance in chloride-bearing environments, particularly in the 50–100°C range, a known danger zone for austenitic grades.
8. Výroba & Machináovateľnosť
CNC obrábanie
CF3 machines comparably to wrought 304, with a machinability index of ~45 % (kdekoľvek 304 equals 50 %).
Shops typically use carbide tools, cutting speeds of 100–150 m/min, and feeds of 0.12–0.18 mm/rev, delivering surface finishes around Ra 1.6 µm.
Zváranie
Fabricators weld CF3 using 309 alebo 312 filler alloys without preheat.
Post‑weld annealing at 1,050 °C for one hour restores corrosion resistance, reducing delta‑ferrite and dissolving weld‑zone carbides.
Formujúci & Príbuzný
Although CF3’s work‑hardening rate lags that of carbon steel, it tolerates cold forming reductions up to 40 %.
To prevent springback, designers recommend bend radii of at least 3× material thickness.
9. Applications of CF3 Stainless Steel
Ventily, Čerpadlá, and Fittings in Water Treatment
In municipal and industrial water treatment facilities, CF3 stainless steel is a material of choice for:
- Telá a kapoty
- Pumpa a obežné kolesá
- Pipe fittings and couplings
Its resistance to chloride-induced corrosion, even in brackish or mildly saline environments, ensures long service life with minimal maintenance.
The low carbon content reduces the risk of sensitization during welding, which is critical for pressure-retaining systems.
Petrochemical and Oil & Gas Components
The oil and gas industry frequently uses CF3 for castings that encounter corrosive fluids, including hydrocarbons, hydrogen sulfide, and CO₂-rich environments. Bežné aplikácie zahŕňajú:
- Kompresorové kryty
- Manifolds and flowline components
- Metering valves and flanges
In up- and midstream systems, CF3 helps prevent stress-corrosion cracking (Scc) a jamka, which are accelerated by high chloride content or wet sour gas.
Food Processing and Pharmaceutical Equipment
Hygienic process systems require materials with excellent corrosion resistance, povrchová povrchová úprava, and compatibility with cleaning agents (Cip/dúšok). CF3 fits these requirements, čo je vhodné pre:
- Sanitary valves and pipe fittings
- Mixing and metering equipment
- Dosing pumps and housings
Svoj austenitická mikroštruktúra, which remains stable even after repeated sterilization cycles, helps meet FDA a 3-Sanitárne štandardy in critical production environments.
Power Generation and Marine Hardware
- Steam and condensate system components
- Seawater pumps and valve parts
- Heat exchanger end covers
Its resistance to aqueous corrosion, biofouling, a oxidation at elevated temperatures enhances component longevity in these aggressive settings.
V morskom prostredí, CF3 performs reliably in both surface and submerged service.
Other Emerging Applications
- Hydrogen handling systems: Due to its non-magnetic and crack-resistant nature
- Semiconductor wet-processing tools: Where ultra-clean, non-reactive materials are needed
- Additive-manufactured cast components: For reduced weight and complex design integration
10. Porovnanie s alternatívnymi materiálmi
Selecting the appropriate stainless steel grade for a given application requires a deep understanding of the performance trade-offs between available options.
CF3 stainless steel, as the low-carbon cast equivalent of 304L, is often compared to related alloys such as Cf3m, CF8, CF8M, and wrought 304 nerezový.
| Majetok | Cf3 (304Odliať) | Cf3m (316Odliať) | CF8 (304 Vrhnúť) | CF8M (316 Vrhnúť) | 304L Wrought |
|---|---|---|---|---|---|
| Molybdén (Mí) Spokojnosť | Nie | Áno | Nie | Áno | Nie |
| Obsah | ≤ 0.03% (Nízkohlíkový) | ≤ 0.03% (Nízkohlíkový) | ≤ 0.08% | ≤ 0.08% | ≤ 0.03% (Nízkohlíkový) |
| Odpor | Mierny | Vynikajúci | Mierny | Vynikajúci | Mierny |
| Odpor (Drevo) | ~ 18 | ~ 25–27 | ~ 20 | ~ 25–27 | ~ 18 |
| Odpor | Dobre | Vynikajúci | Mierny | Vynikajúci | Dobre |
| Zvárateľnosť | Vynikajúci | Vynikajúci | Mierny | Mierny | Vynikajúci |
| Náklady | $$ | $$$ | $$ | $$$ | $$ |
| Pevnosť (Ťah) | ~ 485 MPa | ~500 MPa | ~510 MPa | ~ 520 MPa | ~ 520 MPa |
| Predĺženie | ~ 40% | ~ 45% | ~ 45% | ~ 45% | ~ 45% |
| Formovateľnosť | Excellent for cast parts | Excellent for cast parts | Good for cast parts | Good for cast parts | Vynikajúci (for rolled or formed parts) |
| Žiadosti | Water systems, food-grade parts | Chemický, námorný, pobrežie | General industrial parts | Morský, chemický, pobrežie | High-ductility, tenkostenné diely |
11. Záver
V súhrne, CF3 stainless steel merges the proven corrosion resistance of 304 with the versatility of casting.
Its balanced chemistry, robust mechanical profile, and proven long‑term durability make CF3 an authoritative choice for medium‑duty corrosive environments.
Navyše, with annual global production exceeding 50,000 tonnes and scrap rates under 6 %, CF3 delivers both economic and performance advantages.
Tešiť sa, integrating CF3 into hybrid casting–additive workflows and exploring surface treatments promises to extend its service envelope—ensuring CF3 remains a cornerstone alloy in industrial applications.
LangHe je ideálna voľba pre vaše výrobné potreby, ak potrebujete kvalitnú kvalitu odliatky z nehrdzavejúcej ocele.
FAQs on CF3 Stainless Steel
Is CF3 Stainless Steel suitable for high-temperature applications?
CF3 is generally suitable for moderate-temperature applications (up to about 800°F or 427°C).
For higher temperatures, or when oxidácia at elevated temperatures is critical,
other grades like CF8M alebo 316 nehrdzavejúca oceľ may be more appropriate due to their enhanced high-temperature properties.
Can CF3 be welded?
Áno, CF3 stainless steel is highly zvárateľný. Its low carbon content minimizes the risk of carbide formation during welding, reducing the chances of intergranular corrosion.
Avšak, it is always recommended to use appropriate welding techniques a post-weld heat treatments when working with this material in critical applications.
Is CF3 Suitable for Cryogenic Applications?
Áno, CF3 exhibits good toughness at low temperatures, making it suitable for use in cryogenic applications such as liquefied natural gas (Lng) storage and transportation.
Can CF3 Be Heat Treated?
CF3 is generally not heat treatable for strengthening purposes. Avšak, it can be annealed to relieve stresses and improve machinability.
How does CF3 Stainless Steel perform in seawater?
CF3 offers moderate resistance to seawater corrosion, but it is not as resistant as CF3M or CF8M, which have enhanced chloride resistance due to the presence of molybdén.
V morské prostredie with high salinity, CF3 may experience some korózia jamiek časom, so CF3M or CF8M might be more suitable.
How should CF3 Stainless Steel be maintained?
Regular maintenance of CF3 stainless steel includes:
- Čistenie: Removing contaminants such as chlorine, soľ, and chemicals that could cause localized corrosion.
- Kontrola: Checking for any signs of jamka alebo korózia trhliny, najmä v námorný alebo chemical environments.
- Zváranie: Ensuring proper po zváraní tepelné spracovanie to avoid cracking or sensitization.
Can CF3 Stainless Steel be used in food contact applications?
Áno, CF3 is often used in vybavenie na spracovanie potravín kvôli odpor a ease of cleaning.
It complies with FDA a 3-Sanitárne štandardy, urobiť z neho vhodnú voľbu pre sanitárny ventily, čerpadlá, a potrubné systémy.