Among the four main families of stainless steel, martensitic stainless steel occupies a unique and distinguished position.
Unlike austenitic grades, which cannot be hardened by heat treatment, or ferritic grades, which offer limited hardenability, martensitic stainless steels are hardenable by heat treatment—capable of achieving high hardness, izturība, and wear resistance through quenching and tempering.
This combination of corrosion resistance and mechanical performance makes them the material of choice for applications requiring both durability and resistance to aggressive environments.
From cutlery and surgical instruments to turbine blades and automotive components, martensitic stainless steels are indispensable in countless industrial and consumer applications.
1. Kas ir martensīta nerūsējošais tērauds?
Martensīts nerūsējošais tērauds is a category of stainless steel that can develop a predominantly martensitic microstructure through heat treatment.
It is generally classified separately from austenitic, ferīta, divstāvu, and precipitation-hardening stainless steels because its primary strengthening mechanism is based on the transformation of austenite into martensite during cooling, followed by tempering to achieve the required balance of mechanical properties.
In simplified terms, the manufacturing and heat-treatment sequence follows the transformation:
Annealed Structure → Austenitizing → Quenching → Martensitic Structure → Tempering → Final Engineering Properties
The process begins by heating the steel to an appropriate austenitizējoša temperatūra, where the microstructure transforms into austenite and alloying elements redistribute according to the composition and thermal cycle.
The component is then cooled rapidly enough to suppress the formation of softer equilibrium structures and promote martensitic transformation.
The resulting martensite is characterized by a highly strained crystal structure containing supersaturated carbon.
This produces high hardness and strength, but freshly quenched martensite may also have limited toughness and significant residual stress.
Līdz ar to, martensitic stainless steel components are commonly subjected to rūdījums, which reduces brittleness and allows engineers to tailor the final hardness and toughness.
The Martensitic Transformation
The martensitic transformation is a diffusionless, shear‑type transformation that occurs when austenite (FCC) is rapidly cooled below the martensite start temperature (MS).
The transformation is instantaneous and does not involve diffusion of carbon atoms—carbon remains trapped in the lattice, creating a supersaturated solid solution.
| Skatuve | Apraksts | Temperatūra |
| Austenitising | Heating to 950–1050°C to form austenite. | 950–1050 ° C |
| Rūdīšana | Ātra dzesēšana (eļļas, gaisa, or water) to transform austenite to martensite. | Below Ms |
| Rūdījums | Re‑heating to 150–650°C to relieve stress and adjust properties. | 150–650 ° C |
2. Chemical Composition of Martensitic Stainless Steel
Since martensitic stainless steel covers a broad family of grades, the ranges below are representative industry ranges rather than requirements for any single grade.
| Alloying Element | Parasti diapazons (WT%) | Primary Function in Martensitic Stainless Steel |
| Hroms (Krekls) | 10.5–18,0% | Provides the fundamental corrosion and oxidation resistance of stainless steel and strongly influences phase stability. |
| Ogleklis (C) | 0.03–1,20% | Primary hardening and strengthening element in conventional martensitic grades. |
| Niķelis (Iekšā) | 0–3,0% | Uzlabo izturību, Sacietējamība, and phase stability in selected grades. |
| Molibdēns (Noplūde) | 0–1.5% | Enhances localized corrosion resistance and contributes to hardenability and elevated-temperature performance. |
| Mangāns (Nojaukšanās) | 0–1.5% | Supports deoxidation and influences austenite stability and hardenability. |
Silīcijs (Un) |
0–1,0% | Primarily acts as a deoxidizer during steelmaking and can contribute to oxidation resistance. |
| Slāpeklis (N) | 0–0,20% | Strengthening and austenite-stabilizing element used in selected modern or specialized grades. |
| Vanādijs (V) | 0–1,0%* | Strong carbide-forming element used mainly in specialized high-wear or tool-type martensitic steels. |
| Niobijs (Nb) | 0–1,0%* | Forms stable carbides and can improve metallurgical stability in selected grades. |
Ogleklis: The Primary Hardening Element
Carbon has an especially important role in martensitic stainless steel because it strongly affects the structure formed during heat treatment.
In the annealed condition, carbon may exist partly in solid solution and partly in carbide phases, depending on the grade and thermal history.
During austenitizing and subsequent quenching, carbon contributes to the formation of hard martensite.
As a general engineering trend:
- Lower carbon levels favor improved toughness and more moderate hardness.
- Medium carbon levels provide a balance between hardness and mechanical strength.
- High carbon levels enable very high hardness and improved wear resistance but can reduce toughness and increase brittleness.
This is why grades within the martensitic family can have dramatically different applications.
A relatively low-carbon grade may be used for valves, vārpstas, un strukturālās sastāvdaļas, while a high-carbon grade may be selected for knives, griešanas rīki, and wear-resistant precision parts.
3. Major Types and Grades of Martensitic Stainless Steel
Martensitic stainless steel includes several distinct grade groups developed to meet different requirements for hardness, izturība, izturība pret koroziju, nodilums pretestība, mašīnīgums, izturība, un liešana.
Standard Martensitic Grades
The composition ranges below are representative limits commonly associated with the corresponding grade designations.
Exact requirements should always be verified against the applicable ASTM, Iekšā, Mūs, Viņš ir, or customer specification.
| Pakāpe | ASV apzīmējums | Approximate Composition | Tipiskas lietojumprogrammas |
| 410 | S41000 | Krekls: 11.5–13.5%; C: ≤0.15% | Vārsti, sūkņa komponenti, vārpstas, stiprinājumi, turbīnu daļas, and general industrial components. |
| 420 | S42000* | Krekls: 12–14%; C: 0.15–0.40% | Galda piederumi, ķirurģiski instrumenti, asmeņi, veidnes, un nodilumizturīgiem komponentiem. |
| 420J2 | Commonly associated with S42000-family equivalents** | Krekls: 12–14%; C: 0.26–0.40% | Naži, šķēres, shears, consumer cutlery, and general-purpose cutting tools. |
| 431 | S43100 | Krekls: 15–17%; Iekšā: 1.25–2.50%; C: ≤0.20% | Sūkņu vārpstas, jūras vārpstas, vārstu komponenti, lidmašīnu veidgabali, and high-strength mechanical parts. |
440Izšķirt |
S44002 | Krekls: 16–18%; C: 0.60–0.75% | Galda piederumi, vārstu komponenti, gultņi, medicīnas instrumenti, and wear-resistant parts. |
| 440Bārts | S44003 | Krekls: 16–18%; C: 0.75–0,95% | Griešanas rīki, precision instruments, gultņi, un valkājiet komponentus. |
| 440C | S44004 | Krekls: 16–18%; C: 0.95–1,20% | High-performance bearings, precision wear components, premium cutlery, valve parts, un ķirurģiski instrumenti. |
| 416 | S41600 | Krekls: 12–14%; C: ≤0.15%; S: 0.15–0.35% | Precision-machined fittings, vārpstas, skrūvju skrūve, vārstu komponenti, stiprinājumi, and automatic-screw-machine parts. |
Cast Martensitic Grades
The ASTM casting designation system identifies several important martensitic stainless steel grades.
| ASTM Cast Grade | ASV apzīmējums | Approximate Composition | Tipiskas lietojumprogrammas |
| CA-15 | J91150 | Krekls: aptuveni 11.5–14,0%; C: parasti ≤0.15% | Valve bodies and trim, sūkņa komponenti, turbīnu daļas, hydraulic equipment, un rūpnieciskā mašīna. |
| CA-40 | J91151 | Krekls: aptuveni 11.5–14,0%; C: parasti līdz 0.40% | Wear-resistant valve parts, rūpnieciskā mašīna, steam-service components, and mechanical parts. |
CA-6NM |
J91540 | Krekls: aptuveni 11.5–14,0%; Iekšā: aptuveni 3.5–4.5%; Noplūde: aptuveni 0.4–1,0%; C: ≤0,06% | Hidrauliskās turbīnas, hydroelectric equipment, large pump impellers, sūkņu apvalki, and water-handling components. |
| CB-7Cu-1 | J92180 | Krekls: aptuveni 14–16%; Iekšā: aptuveni 4–6%; Cu: aptuveni 2.5–4,0%; C: ≤0.07% | Aviācijas un kosmosa komponenti, high-strength castings, sūkņi, vārsti, and demanding industrial equipment. |
4. Heat Treatment of Martensitic Stainless Steel
Termiskā apstrāde is one of the defining aspects of martensitic stainless steel.
Unlike austenitic stainless steels, which generally cannot be significantly strengthened by conventional quenching and tempering,
martensitic grades are specifically designed to develop different combinations of cietība, izturība, izturība, nodilums pretestība, un dimensiju stabilitāte through controlled thermal processing.
Rūdīšana
Annealing is commonly used to soften martensitic stainless steel before machining, veidošanās, or subsequent heat treatment.
Depending on the grade and specification, the steel is heated into an appropriate temperature range and cooled under controlled conditions to produce a softer and more machinable microstructure.
The primary objectives of annealing include:
- Reducing hardness
- Relieving internal stress
- Improving machinability
- Improving dimensional stability
- Producing a more uniform microstructure before final hardening
For many components, rough machining is performed in the annealed condition because fully hardened martensitic stainless steel can be difficult and expensive to machine.
The component is subsequently heat treated and then finish-machined or ground to achieve the required final dimensions.
Austenitizējošs
Austenitizing is the stage at which the steel is heated to form austenite before quenching. The required temperature depends strongly on the grade.
For common martensitic stainless steels, typical austenitizing temperatures may fall approximately within the following ranges:
| Grade Family | Typical Austenitizing Range* | Primary Objective |
| 410 / low-carbon martensitic grades | Aptuveni 925–1,010°C | Develop an austenitic structure suitable for subsequent hardening. |
| 420 / medium-carbon grades | Aptuveni 980–1,065°C | Dissolve an appropriate amount of carbon and alloying elements before quenching. |
| 440-series high-carbon grades | Aptuveni 1,010–1,120 ° C | Develop high hardness potential while controlling carbide dissolution and grain growth. |
| 431 and nickel-containing grades | Aptuveni 980–1,070°C | Develop a suitable balance of hardenability, izturība, un izturība. |
* These ranges are representative only. Actual heat-treatment temperatures and holding times should be selected according to the applicable material specification, sekcijas izmērs, furnace conditions, and required final properties.
Austenitizing must be carefully controlled. Ja temperatūra ir pārāk zema, insufficient transformation or carbide dissolution may limit the attainable hardness.
Excessively high temperatures or excessive holding times may promote grain growth and increase the amount of retained austenite, potentially reducing toughness and dimensional stability.
Rūdīšana
After austenitizing, the component is cooled at a rate sufficient to promote the transformation of austenite into martensite.
Depending on the grade and component geometry, quenching may involve:
- Gaisa dzesēšana
- Oil quenching
- Polymer quenching
- Pressurized gas quenching
- Other controlled cooling methods
The selection of quenching medium is a balance between achieving sufficient cooling for hardening and minimizing thermal stress.
Rūdījums
Freshly quenched martensite can have very high hardness but also high internal stress and limited toughness.
Tempering is therefore an essential step for most engineering applications.
During tempering, the steel is reheated to a controlled temperature below the austenitizing range and held for an appropriate period.
The process allows the martensitic structure to stabilize and reduces residual stresses while adjusting the balance between hardness and toughness.
Vispār:
- Lower tempering temperatures tend to retain higher hardness and wear resistance.
- Higher tempering temperatures generally reduce hardness while improving toughness and stress stability.
The precise relationship is grade-dependent. Some martensitic stainless steels can also exhibit undesirable embrittlement or changes in corrosion behavior within particular tempering ranges.
Tāpēc, tempering temperature should be selected according to the relevant grade specification and required service properties rather than based solely on a general hardness target.
Double Tempering and Dimensional Stabilization
High-carbon and high-performance martensitic stainless steels may require multiple tempering cycles to improve structural stability and reduce retained austenite effects.
Double tempering can provide several benefits:
- Improved dimensional stability
- More uniform mechanical properties
- Reduced residual stress
- Stabilization of transformed retained austenite
- Improved balance between hardness and toughness
In precision applications, additional stabilization treatments may be used before final grinding or finishing.
This is particularly important for bearings, griešanas rīki, precision valve components, and other parts where small dimensional changes can affect functional performance.
5. Typical Mechanical Property Ranges of Martensitic Stainless Steel
The following values provide representative engineering ranges for commonly used martensitic stainless steels.
Actual properties vary according to product form, sekcijas biezums, termiskā apstrāde, tempering condition, and applicable standard.
| Pakāpe | Typical Condition | Peļņas izturība, RP0.2 (MPA) | Stiepes izturība, Rm (MPA) | Elongation A (%) | Cietība |
| 410 | Rūdīts & rūdīts | 550–1 000 | 700–1 200 | 10–20 | Apm.. 25–45 HRC |
| 416 | Rūdīts & rūdīts | 550–1 000 | 700–1 200 | 10–20 | Apm.. 25–45 HRC |
| 420 | Rūdīts & rūdīts | 700–1,300 | 900–1,600 | 8–18 | Apm.. 45–55 HRC |
| 431 | Rūdīts & rūdīts | 700–1 000 | 900–1 200 | 10–20 | Apm.. 28–45 HRC |
| 440Izšķirt | Rūdīts & rūdīts | 1,000-1500 | 1,500–1,900 | 5–12 | Apm.. 54–58 HRC |
| 440Bārts | Rūdīts & rūdīts | 1,100-1500 | 1,600–1,950 | 4–10 | Apm.. 56–59 HRC |
| 440C | Rūdīts & rūdīts | 1,200–1,600 | 1,800–2,000+ | 2–8 | Apm.. 56–60 HRC |
| CA-15 | Atlaist, termiski apstrādāts | ≥450 | ≥620 | ≥18 | Parasti ~180–230 HB |
6. Characteristics of Martensitic Steel
Izturība pret koroziju
Tāpat kā visi nerūsējošie tēraudi, martensitic grades derive corrosion protection from a thin, self-healing chromium oxide passive film.
Tomēr, their performance sits below that of austenitic grades:
- They provide good resistance to rural and light urban atmospheres, neutral fresh water, mild organic acids and most food environments.
- Their lower chromium content (12–14% for standard grades) and chromium carbide precipitation result in poorer pitting resistance and general corrosion resistance compared with 18/8 austenitic steels.
- They are unsuitable for prolonged exposure to seawater, strong mineral acids, high-chloride solutions or heavy industrial atmospheres.
- Higher-chromium grades such as 440C offer better corrosion performance than lower-chromium 410 un 420, despite higher carbon content.
Magnētiskās īpašības
Martensitic stainless steels are strongly magnetic in all heat treatment conditions.
This is a direct consequence of their body-centered tetragonal crystal structure, which supports spontaneous magnetic ordering from unpaired electron spins.
A common misconception is that magnetic response indicates low-quality stainless steel.
Patiesībā, magnetism is a structural property, not a quality indicator: all martensitic and ferritic stainless steels are naturally magnetic, including high-performance grades like 440C.
Wear Resistance and Hardness
Excellent wear resistance is the flagship advantage of high-carbon martensitic grades.
When hardened to 55+ HRC, they outperform austenitic and ferritic stainless steels by a factor of 5–10 in both abrasive and adhesive wear applications.
The combination of hard martensitic matrix and dispersed chromium carbide particles creates a material that retains its shape and surface finish under repeated sliding contact.
This makes martensitic stainless the only viable stainless steel option for cutting edges, bearing surfaces and sliding contact components.
Weldability of Martensitic Stainless Steel
Weldability is generally considered the most significant processing limitation of martensitic stainless steels:
- The high hardenability of the alloy means weld metal and heat-affected zones harden rapidly upon cooling, creating high residual tensile stress and high risk of cold cracking.
- Standard welding procedures require preheating to 200–300°C, controlled interpass temperature and mandatory post-weld tempering immediately after welding to prevent failure.
- Low-carbon grade 410 has the best weldability within the family; high-carbon 440C is generally not recommended for fusion welding.
- Kritiskām lietojumprogrammām, matching martensitic filler metals or austenitic 309/310 fillers are used to reduce cracking risk.
Machinability and Formability
- Mašīnīgums varies strongly with hardness. In the fully annealed condition, martensitic stainless steels have good machinability, generally better than austenitic 304 due to a lower work-hardening rate.
In the hardened condition, machinability is very poor; nearly all finish machining should be completed in the soft annealed state before hardening.
Free-machining grade 416 offers significantly improved chip breaking and tool life for high-volume screw machine production. - Formīgums is moderate in the annealed state, suitable for bending, roll forming and shallow drawing operations.
Martensitic grades cannot match the deep drawability of austenitic steels, and cold forming must always be performed before hardening.
7. Manufacturing Processes for Martensitic Stainless Steel Components
Martensitic stainless steel can be processed through a wide range of manufacturing routes, ieskaitot CNC apstrāde, investīciju liešana, smilšu liešana, kalšana, and powder metallurgy.
The appropriate process depends on component geometry, Dimensijas prasības, ražošanas apjoms, mechanical-property requirements, material utilization, and whether the component will undergo subsequent hardening and tempering.
CNC apstrāde
CNC apstrāde is a subtractive manufacturing process in which martensitic stainless steel is removed from bar, plāksne, kalšana, or other semi-finished stock using computer-controlled cutting tools.
Common operations include pagrieziens, frizēšana, urbšana, vītņošana, garlaicīgs, slīpēšana, and multi-axis machining.
Martensitic stainless steel is frequently machined in the annealed or softened condition before final hardening.
Rough machining can then be followed by quenching and tempering, with finish machining or grinding used to achieve the final dimensional and surface requirements.
Investīciju liešana
Investīciju liešana, pazīstams arī kā zaudēto vaska liešana, produces martensitic stainless steel components by creating a detailed wax pattern, forming a ceramic shell around the pattern, removing the wax, and pouring molten stainless steel into the resulting cavity.
The process is especially useful for components with sarežģīta ģeometrija, plānas sekcijas, iekšējie fragmenti, integrētie priekšnieki, and difficult-to-machine profiles.
Smilšu liešana
Smilšu liešana uses a sand mold to form the cavity into which molten martensitic stainless steel is poured.
Compared with investment casting, sand casting provides greater flexibility for larger components and relatively simple or moderately complex geometries.
It is widely used for industrial components where structural integrity, component size, and manufacturing economics are more important than extremely fine surface detail.
Kalšana
Kalšana forms martensitic stainless steel through controlled plastic deformation, normally at elevated temperature.
The material is compressed between dies or other tooling to produce the required geometry.
Forging can generate a refined and directional microstructure while reducing internal porosity and improving structural integrity.
It is therefore frequently selected for components exposed to Augstas mehāniskās slodzes, trieciens, spiediens, or cyclic stresses.
Typical forged components include shafts, vārsta kāti, sūkņu vārpstas, stiprinājumi, armatūra, and high-strength mechanical components.
Pulvera metalurģija
Pulvera metalurģija produces high-carbon martensitic grades such as 440C with extremely uniform carbide distribution and fine grain structure, outperforming wrought material in wear resistance and dimensional stability.
The process is ideal for small, complex high-wear components where conventional machining would be prohibitively expensive.
8. Surface Finishes and Surface Engineering
Martensitic stainless steels are compatible with a full range of surface finishing and engineering treatments to enhance appearance, corrosion resistance and wear performance:
- Mill finish: Standard as-rolled or as-forged surface for industrial structural parts
- Mehāniska pulēšana / spoguļa apdare: High-carbon grades can be polished to optical-quality mirror surfaces, making them the standard for surgical instruments and high-end cutlery
- Sakropļots / satīna apdare: Directional textured finish for hand tools and decorative hardware
- Pasniegšana: Chemical treatment to remove free iron and enhance the passive oxide layer, Korozijas pretestības uzlabošana
- Elektropolēšana: Īpaši gludi, corrosion-resistant surface finish for medical and food-contact components
- Cietie pārklājumi: DLC, TiN and chromium carbide coatings further increase surface hardness and reduce friction for severe-wear bearing and cutting applications
9. Applications of Martensitic Stainless Steel
Martensitic stainless steel is widely used where a component requires a combination of high strength, cietība, nodilums pretestība, Mērena izturība pret koroziju, un dimensiju stabilitāte.
Valves and Fluid-Control Equipment
Martensitic stainless steel is widely used for vārsta kāti, valve trim, sēdekļi, vārpstas, and other internal components.
Its high hardness helps resist erosion, nodilums, and repeated mechanical contact, while its corrosion resistance provides protection in many water, tvaika, and industrial-fluid environments.
Typical components include:
- Vārsta kāti
- Valve balls and trim
- Sēdekļi
- Sūkņu vārpstas
- Lāpstiņriteņi
- Bukses
- Wear rings
Cutlery and Cutting Tools
High-carbon martensitic grades are particularly important in knives and cutting applications.
420 is widely used for general-purpose blades, kamēr 440Izšķirt, 440Bārts, and 440C can provide higher hardness and wear resistance.
The key advantages are:
- High edge retention
- Augsta cietība
- Resistance to deformation
- Laba nodiluma pretestība
- Reasonable corrosion resistance compared with conventional carbon tool steels
Bearings and Precision Wear Components
High-carbon martensitic stainless steels, particularly 440C, are used for corrosion-resistant bearing components.
Tipiskas lietojumprogrammas ietver:
- Bearing balls
- Bearing races
- Precision rollers
- Bukses
- Wear rings
- Instrument bearings
Medical and Surgical Instruments
Martensitic stainless steels are widely used in surgical instruments because they can combine cietība, edge retention, izturība, izturība pret koroziju, and sterilization capability.
Pieteikumos ietilpst:
- Surgical scissors
- Ķirurģiskas asmeņi
- Forceps
- Skavas
- Dental instruments
- Cutting instruments
Automobiļu komponenti
Martensitic stainless steel can be used in automotive components exposed to mechanical loads, sildīt, valkāt, un kodīga vide.
Pieteikumos ietilpst:
- Vārpstas
- Vārstu komponenti
- Sūkņa komponenti
- Stiprinājumi
- Exhaust-related components
- Mechanical actuators
- Nodiluma izturīgas sastāvdaļas
Aerospace and Turbine Components
Selected martensitic stainless steels are used in aerospace and energy equipment where high strength and dimensional stability are required.
Applications can include:
- Turbīnu komponenti
- Vārpstas
- Stiprinājumi
- Sūkņa komponenti
- Actuation components
- High-strength mechanical parts
Enerģija, Sūknēt, and Hydroelectric Equipment
Martensitic stainless steels are also important in energy-generation and water-handling equipment.
The cast grade CA-6NM, piemēram, is a low-carbon martensitic stainless steel containing nickel and molybdenum and is widely associated with hydraulic turbine runners, sūkņa komponenti, and water-handling equipment.
10. Advantages and Limitations of Martensitic Stainless Steel
Martensitic stainless steel is distinguished from other stainless steel families by its ability to develop high strength and hardness through quenching and tempering.
This makes it particularly suitable for components exposed to wear, mechanical loading, griezt, trieciens, and repeated contact.
Tomēr, the same metallurgical characteristics that provide high hardness can reduce ductility, izturība, izturība pret koroziju, un metināmība.
Galvenās priekšrocības
- The only stainless steel family hardenable by heat treatment, with tunable hardness from 20 HRC to 62 HRC
- Excellent wear resistance and surface hardness, 5–10 times superior to austenitic stainless steels
- 2–3 times higher strength than standard austenitic grades in hardened condition
- Mērena izturība pret koroziju, significantly better than plain carbon steel
- Naturally magnetic, suitable for magnetic component applications
- Excellent polishability to high-gloss mirror finishes
- Lower cost than high-alloy austenitic and duplex stainless steels for equivalent strength levels
Inherent Limitations
- Lower general and pitting corrosion resistance compared with 304/316 austenītiskās pakāpes; unsuitable for high-chloride and strong acid environments
- Poor weldability requiring preheat and post-weld tempering to avoid cracking
- Requires heat treatment to achieve optimal properties, adding processing cost and lead time
- Lower ductility and toughness than austenitic stainless steels in hardened condition
- Susceptible to temper brittleness in specific temperature ranges
- Limited deep-drawing and cold-forming capability
11. Martensitic vs. Austenitic vs. Ferīta nerūsējošā tērauda
The three major stainless steel families differ primarily in microstructure, heat-treatment response, izturība, izturība pret koroziju, elastība, magnētiskā uzvedība, un metināmība.
The following table focuses on the engineering characteristics most relevant to material selection.
| Īpašums | Martensīta nerūsējošais tērauds | Austenīta nerūsējošais tērauds | Ferīta nerūsējošā tērauda |
| Tipiskas pakāpes | 410, 420, 431, 440A/440C | 304, 304Lukturis, 316, 316Lukturis, 321 | 409, 430, 439, 441, 444 |
| Kristāla struktūra | BCT martensite after hardening | FCC austenīts | BCC ferīts |
| Typical Cr Content | ~11.5–18 wt% | ~16–26 wt% | ~10.5–30 wt% |
| Heat-Treatment Hardening | Lielisks; rūdīts un rūdīts | Not hardenable by conventional quenching | Not hardenable by conventional quenching |
| Izturība | Augsts līdz ļoti augsts | Mērens; higher strength achievable by cold working | Mērens |
| Cietība | Augsts, typically ~20–60+ HRC depending on grade and condition | Generally lower in annealed condition | Generally moderate |
| Elastība & Izturība | Moderate to low when highly hardened | Lielisks | Mērens |
| Izturība pret koroziju | Mēreni vai labi | Excellent to very good | Good for many atmospheric environments |
| Nodilums pretestība | Excellent when hardened | Mērens | Mērens |
| Magnētiskās īpašības | Magnētisks | Generally non-magnetic when annealed | Magnētisks |
| Metināmība | Mēreni vai nabadzīgi; heat-treatment control may be required | Lielisks, particularly low-carbon grades | Labs līdz mērens |
| Formīgums | Mērens; limited severe forming | Lielisks, including deep drawing | Labs līdz mērens |
Mašīnīgums |
Good when annealed; difficult after hardening | Mērens; work hardening can complicate machining | Generally good to moderate |
| Low-Temperature Performance | Grade-dependent; high-carbon grades can have limited toughness | Lielisks | More limited because of the ductile-to-brittle transition |
| Tipiskas lietojumprogrammas | Naži, vārpstas, vārsti, sūkņi, gultņi, ķirurģiski instrumenti, valkāt daļas | Ķīmiskais aprīkojums, Pārtikas apstrādes aprīkojums, spiediena tvertnes, cauruļvadi, arhitektūras komponenti | Automobiļu izplūdes sistēmas, ierīces, arhitektūras paneļi, siltummaiņi |
| Main Advantage | Lielas izturības, cietība, un nodiluma pretestība | Augstāka izturība pret koroziju, elastība, izturība, un metināmība | Laba izturība pret koroziju, low thermal expansion, magnētiskās īpašības, un izmaksu efektivitāte |
| Main Limitation | Lower corrosion resistance and weldability | Lower hardness in the annealed condition; Ni-containing grades can be more expensive | Lower toughness and formability than austenitic grades |
12. Custom Martensitic Stainless Steel Parts from LangHe
LangHe provides customized manufacturing solutions for martensitic stainless steel components, combining material selection, precīza liešana, CNC apstrāde, termiskā apstrāde, and surface finishing to produce components tailored to specific mechanical and dimensional requirements.
| Spēja | Detaļa |
| Martensitic Stainless Steel Grades | 410, 420, 431, 440Izšķirt, 440Bārts, 440C and selected cast martensitic grades |
| Ražošanas procesi | Investīciju liešana, smilšu liešana, CNC pagrieziens, CNC frēzēšana, urbšana, grinding and related secondary operations |
| Termiskā apstrāde | Rūdīšana, sacietēšana, quenching and tempering according to grade and required mechanical properties |
| Apstrāde | CNC pagrieziens, frizēšana, urbšana, vītņošana, garlaicīgs, grinding and precision finishing |
Virsmas apdare |
Pulēšana, slīpēšana, passivation and selected functional surface treatments |
| Component Types | Vārstu komponenti, sūkņa daļas, vārpstas, bukses, wear components, mechanical fittings, tooling and precision industrial parts |
| Kvalitātes kontrole | Iso 9001:2015 sertificēts; 100% NDT and dimensional inspection. |
| Pielāgošana | Production according to customer drawings, 3D CAD modeļi, specifikācija, samples or application requirements |
13. Secinājums
Martensitic stainless steel occupies a unique and irreplaceable position in the stainless steel family.
As the only stainless steel that can be hardened by heat treatment to achieve high strength and excellent wear resistance, it fills the critical performance gap between plain carbon tool steels and corrosion-resistant austenitic stainless steels.
Its corrosion resistance is lower than that of 304 un 316 austenītiskās pakāpes, but it delivers strength and wear performance that no austenitic or ferritic grade can match.
From everyday cutlery to precision surgical instruments, from industrial valves to power generation turbine blades, martensitic stainless steels deliver targeted performance where moderate corrosion resistance must be combined with high strength and wear durability.
As alloy design and heat treatment technology continue to advance, new toughened, high-purity and precipitation-hardened martensitic grades will continue to expand the material family’s application scope, reinforcing its status as an essential branch of the global stainless steel ecosystem.
FAQ
What is the difference between martensitic and austenitic stainless steel?
Martensitic stainless steel is hardenable by heat treatment, magnētisks, and has moderate corrosion resistance.
Austenitic stainless steel is not hardenable by heat treatment, nemagnētisks, and has excellent corrosion resistance.
Martensitic grades are used for cutlery, vārsti, un gultņi; austenitic grades are used for chemical, pārtika, un jūras pielietojums.
Can martensitic stainless steel be welded?
Jā, bet ar piesardzību. Preheating and post‑weld heat treatment are required to prevent cracking and restore mechanical properties.
Is martensitic stainless steel magnetic?
Jā. All martensitic stainless steels are ferromagnetic (strongly attracted to magnets).
Does martensitic stainless steel rust?
Martensitic stainless steel can stain and corrode under aggressive conditions.
It resists rust in normal atmospheric and fresh-water environments, but will develop surface staining and pitting in high-salt, strong-acid or heavy industrial settings.
It is not suitable for prolonged seawater immersion or continuous chloride exposure.
Can martensitic stainless steel be heat treated?
Jā. Heat treatment is one of the defining characteristics of this stainless steel family.
Depending on the grade, hardening followed by tempering can substantially increase hardness, stiepes izturība, un nodiluma pretestība.
Which martensitic stainless steel is the hardest?
Among common martensitic stainless steels, 440C is one of the highest-carbon grades and can achieve very high hardness after appropriate heat treatment.
Its high hardness makes it particularly suitable for bearings, griešanas rīki, wear components, and high-end blades.