1. Ներածություն
CF3 stainless steel, a member of the austenitic cast stainless steel family, is the low-carbon cast equivalent of the popular wrought grade 304Լ (ԱՄՆ S30403).
It is defined under ASTM A351 and widely used in industries where corrosion resistance, զոդում, and castability are paramount.
Է “C” in CF3 stands for “Corrosion-resistant”, “F” denotes the steel grade (304L equivalent), and the number “3” identifies its low carbon content (≤ 0.03%).
Պատմականորեն, CF3 emerged as part of the response to corrosion issues in chloride-rich and welding-intensive applications.
The introduction of low-carbon grades in the mid-20th century was a milestone that enabled the development of high-integrity welded structures without the need for post-weld heat treatment.
Due to its balanced combination of cost-effectiveness, կատարումը, and resistance to sensitization,
CF3 continues to be strategically important in cast stainless steel applications across chemical, նավթաքիմիական, Treatment րի բուժում, and food-processing sectors.
2. Քիմիական կազմ & Մետալուրգիա
Անվանական քիմիական կազմ
The typical weight percentage (Wt.%) of the alloying elements in CF3 stainless steel, as defined by ASTM A351, է լինել:
| Տարր | Բնորոշ տիրույթ (Wt.%) | Գործառույթ |
|---|---|---|
| Քրոմ (Խուզարկու) | 18.0 Մի քիչ 21.0% | Promotes corrosion resistance through passive film formation |
| Նիկել (Մեջ) | 8.0 Մի քիչ 11.0% | Կայունացնում է օստենիտը, improves ductility and toughness |
| Ածխածնային (Գ) | ≤ 0.03% | Reduces sensitization; improves weldability |
| Մանգան (Ժլատ) | ≤ 1.5% | Enhances hot workability; deoxidizer |
| Սիլիկոն (Մի քանազոր) | ≤ 2.0% | Խթանում է հեղուկը ձուլման մեջ; deoxidizer |
| Ֆոսֆոր (Իմաստ) | ≤ 0.04% | Residual; must be minimized to reduce brittleness |
| Ծծումբ (Ծուռ) | ≤ 0.04% | Residual; excessive S can reduce toughness |
| Երկաթ (Անք) | Հավասարակշռություն | Matrix element |
Է C ածր ածխածնի պարունակություն (≤ 0.03%) significantly mitigates the risk of chromium carbide precipitation at grain boundaries during welding,
making CF3 especially resistant to intergranular corrosion without requiring post-weld heat treatment.
Միկրոկառուցվածք: Austenitic Matrix & Carbide Control
CF3 stainless steel has a fully austenitic microstructure with a face-centered cubic (FCC) lattice, which contributes to:
- Excellent toughness at both ambient and cryogenic temperatures.
- Non-magnetic behavior in the annealed state.
- Resistance to stress corrosion cracking (Շալվար) in many chloride-containing environments.
Due to its low carbon content, CF3 contains minimal chromium carbides, particularly at grain boundaries.
This improves resistance to sensitization, a condition in which chromium-depleted zones form and become vulnerable to corrosive attack.
Some residual delta ferrite (սովորաբար < 10%) may be present after solidification, particularly in sand-cast components.
which helps prevent hot cracking during solidification, but has minimal impact on corrosion resistance or toughness when kept at controlled levels.
3. ASTM A351 CF3 and Global Equivalents
| Ստանդարտ | Նշանակումը | Շրջան | Equivalent Grade |
|---|---|---|---|
| ASTM A351 | Grade CF3 | Ամերիկա | Low-carbon cast 304L |
| ASME SA-351 | Grade CF3 | Ամերիկա (boiler code) | Pressure vessel compliant |
| Մեջ 10283 | Gx2crni19-11 | European Union | Դերասան տարբերակը 1.4306 (304Լ) |
| ISO 11972 | G-X2CrNi19-11 | Միջազգային | Global harmonized equivalent |
| Նա g5121 | SCS13A | Ապոնիա | 304L cast grade |
4. Մեխանիկական հատկություններ
| Մեխանիկական սեփականություն | Բնորոշ արժեք |
|---|---|
| Առաձգական ուժ | ≥485 MPA |
| Բերք տալ ուժ (0.2% փոխհատուցում) | ≥205 MPA |
| Երկարացում | ≥30% |
| Կարծրություն | 140-190 HB |
| Ազդեցության կոշտություն (Room Temp) | > 100 J (Charpy V-Notch) |
| Fatigue Endurance Limit | 240-270 MPA (in air, փայլուն) |
| Սողացող դիմադրություն | Moderate up to 870°C |
Բարձրացված ջերմաստիճանում, tensile and yield strengths decrease gradually, but the alloy retains sufficient structural integrity up to 400–500 °C, making it viable for moderate thermal service.
5. Ջերմային & Ֆիզիկական հատկություններ
| Սեփականություն | Արժեք |
|---|---|
| Խտություն | 7,9 գ / սմ |
| Mal երմային հաղորդունակություն | 16 w / m · k (at 100°C) |
| Coefficient of Expansion | 17.3 μm / m ° ° C (20–400°C) |
| Էլեկտրական դիմադրողականություն | 0.72 ωω · M |
| Magnetic Response | Ոչ մագնիսական (ջղաձգական) |
| Օքսիդացման դիմադրություն | Good up to ~800°C |
6. Casting Characteristics of CF3 Stainless Steel
CF3 stainless steel—cast equivalent of 316—brings molybdenum‑enhanced corrosion resistance into complex geometries.
To harness its full potential, foundries must account for its unique casting behavior, from melt handling to solidification control.
Հեղուկություն & Թափելով ջերմաստիճանը
CF3 melts between 1450 ° C եւ 1550 ° C, slightly higher than CF8 due to its Mo content.
At a pouring superheat of 1500–1560 °C, CF3 achieves a fluidity of 220–280 mm (ISO 243), enabling fill of thin‑walled sections down to 4 մմ.
Այնուամենայնիվ, excessive superheat can increase gas pickup եւ օքսիդացում, so operators typically limit superheat to 50 ° C above liquidus.
Solidification Range & Նեղացում
Հետ freezing range մոտավորապես 60–90 °C, CF3 solidifies over a broader temperature interval than simple austenitic alloys.
Հետեւաբար, it exhibits Գծային նեղացում է 1.9–2.3 %, necessitating careful shrink‑compensation in pattern design.
Կանխել Կենտրոնական ծակոտկենություն, engineers employ Ուղղորդված ամրացում: placing insulated risers above hot spots and using սարսուռ to accelerate freezing in thick sections.
Feeding & Riser Design
Given its moderate shrinkage, CF3 castings benefit from risers sized to feed 30-40 % of the casting mass they support.
Finite‑element thermal simulation often guides riser placement, ensuring uninterrupted metal flow into contracting zones.
Ի հավելումն, Էկզոթերմային թեւեր on critical risers prolong feeding life without increasing overall mold volume.
Շողոքորթություն, Deoxidation & Inoculation
To minimize gas porosity, foundries typically argon‑purge the molten CF3 before pouring.
They also add սիլիկոն (0.3-0.6 %) և ալյումին (0.02–0.05 %) deoxidizers, which form stable oxides and reduce dissolved oxygen.
Վերջապես, a small rare‑earth inoculant (օր., 0.03–0.05 % Fe‑Ce) promotes fine, uniform δ‑ferrite and prevents microshrinkage, enhancing mechanical consistency.
Suitable Casting Methods for CF3 Stainless Steel
| Ձուլման մեթոդ | Բնորոշ ծրագրեր | Առավելությունները | Նկատառումներ |
|---|---|---|---|
| Ավազի ձուլում (Green or No-Bake) | Փական մարմիններ, Պոմպային տներ, եզրեր | – Cost-effective for large parts – Flexible for varied designs |
– Rougher surface finish (Ra 6–12 μm) – Tighter control needed for porosity |
| Shell բորբոս ձուլում | Instrumentation covers, small valves | – Good dimensional accuracy (±0.3%) – Fine surface finish (Ra 3–6 μm) |
– More expensive molds – Best for small to medium-sized parts |
| Ներդրումների ձուլում (Կորցրած մոմը) | Տեղադրում, medical fittings, Բարձր ճշգրտության բաղադրիչներ | – Excellent surface finish (ՀՀ < 3 μm) – High geometric complexity |
– Higher cost – Limited to small–medium parts |
| Կենտրոնախույս ձուլում | Թփեր, օղակներ, pipe sections | – High density – Low porosity – Good mechanical properties in radial direction |
– Suitable only for rotationally symmetric parts |
| Վակուումային ձուլում | Critical components in aerospace, nuclear applications | – Reduced oxidation – Cleaner microstructure |
– Expensive – Requires specialized equipment |
| Կերամիկական բորբոս ձուլում | Complex heat-resistant parts | – Excellent surface detail – Good dimensional precision |
– Longer mold preparation time – Higher cost |
Heat Treatment Practices
Ձուլումից հետո, CF3 typically undergoes Լուծում Օծողավորում Ընդհանուր առմամբ 1040-1120 ° C (1900–2050°F) followed by rapid water quenching. This process serves several purposes:
- Dissolves residual carbides, restoring corrosion resistance
- Homogenizes the microstructure, eliminating segregation from solidification
- Improves ductility and toughness by removing delta ferrite or brittle phases
Strict temperature control during annealing is critical. Insufficient quenching rates can result in զգայունացում և chromium depletion Հացահատիկի սահմաններում, compromising corrosion resistance.
7. Կոռոզիոն դիմադրություն
Ընդհանուր կոռոզիա
In neutral and mildly acidic environments, CF3 maintains excellent resistance due to its chromium-rich passive film. Corrosion rates are typically < 0.05 mm/year in potable water and wastewater systems.
Localized Corrosion Resistance
The alloy shows good performance in environments containing chlorides up to ~200 ppm:
- Pitting դիմադրության համարժեք համարը (Փայտ): ~ 18
- Critical Pitting Temperature (CPT): 20-25 ° C (varies with chloride level)
Սթրես-կոռոզիայից ճեղքումը (Շալվար)
CF3’s low carbon content improves SCC resistance in chloride-bearing environments, particularly in the 50–100°C range, a known danger zone for austenitic grades.
8. Կեղծում & Մեքենայություններ
CNC հաստոցներ
CF3 machines comparably to wrought 304, with a machinability index of ~45 % (որտեղ 304 equals 50 %).
Shops typically use carbide tools, cutting speeds of 100–150 m/min, and feeds of 0.12–0.18 mm/rev, delivering surface finishes around Ra 1.6 սուկ.
Եռակցում
Fabricators weld CF3 using 309 կամ 312 filler alloys without preheat.
Post‑weld annealing at 1,050 °C for one hour restores corrosion resistance, reducing delta‑ferrite and dissolving weld‑zone carbides.
Կազմող & Միանալ
Although CF3’s work‑hardening rate lags that of carbon steel, it tolerates cold forming reductions up to 40 %.
To prevent springback, designers recommend bend radii of at least 3× material thickness.
9. Applications of CF3 Stainless Steel
Փականներ, Պոմպեր, and Fittings in Water Treatment
In municipal and industrial water treatment facilities, CF3 stainless steel is a material of choice for:
- Valve bodies and bonnets
- Pump casings and impellers
- Pipe fittings and couplings
Its resistance to chloride-induced corrosion, even in brackish or mildly saline environments, ensures long service life with minimal maintenance.
The low carbon content reduces the risk of sensitization during welding, which is critical for pressure-retaining systems.
Petrochemical and Oil & Gas Components
The oil and gas industry frequently uses CF3 for castings that encounter corrosive fluids, including hydrocarbons, hydrogen sulfide, and CO₂-rich environments. Common applications include:
- Կոմպրեսորային տներ
- Manifolds and flowline components
- Metering valves and flanges
In up- and midstream systems, CF3 helps prevent stress-corrosion cracking (Շալվար) և թաթ, which are accelerated by high chloride content or wet sour gas.
Food Processing and Pharmaceutical Equipment
Hygienic process systems require materials with excellent corrosion resistance, Հարթ մակերեսի ավարտը, and compatibility with cleaning agents (CIP/SIP). CF3 fits these requirements, այն հարմար դարձնելով:
- Sanitary valves and pipe fittings
- Mixing and metering equipment
- Dosing pumps and housings
Այն austenitic microstructure, which remains stable even after repeated sterilization cycles, helps meet Fda և 3-A Sanitary Standards in critical production environments.
Power Generation and Marine Hardware
- Steam and condensate system components
- Seawater pumps and valve parts
- Heat exchanger end covers
Its resistance to aqueous corrosion, բիոֆուլինգ, և oxidation at elevated temperatures enhances component longevity in these aggressive settings.
In marine environments, CF3 performs reliably in both surface and submerged service.
Other Emerging Applications
- Hydrogen handling systems: Due to its non-magnetic and crack-resistant nature
- Semiconductor wet-processing tools: Where ultra-clean, non-reactive materials are needed
- Additive-manufactured cast components: For reduced weight and complex design integration
10. Համեմատություն այլընտրանքային նյութերի հետ
Selecting the appropriate stainless steel grade for a given application requires a deep understanding of the performance trade-offs between available options.
CF3 stainless steel, as the low-carbon cast equivalent of 304L, is often compared to related alloys such as Cf3m, Cf8, Cf8m, and wrought 304 չժանգոտվող.
| Սեփականություն | CF3 (304Լ դերասան) | Cf3m (316Լ դերասան) | Cf8 (304 Դարակ) | Cf8m (316 Դարակ) | 304L Wrought |
|---|---|---|---|---|---|
| Մոլիբդեն (Ժամանակ) Բովանդակություն | Ոչ | Այո | Ոչ | Այո | Ոչ |
| Ածխածնի պարունակություն | ≤ 0.03% (Ցածր ածխածնի) | ≤ 0.03% (Ցածր ածխածնի) | ≤ 0.08% | ≤ 0.08% | ≤ 0.03% (Ցածր ածխածնի) |
| Քլորիդի դիմադրություն | Չափավոր | Գերազանց | Չափավոր | Գերազանց | Չափավոր |
| Pitting դիմադրություն (Փայտ) | ~ 18 | 25-27 | ~20 | 25-27 | ~ 18 |
| Կոռոզիոն դիմադրություն | Լավ | Գերազանց | Չափավոր | Գերազանց | Լավ |
| Եռակցման հնարավորություն | Գերազանց | Գերազանց | Չափավոր | Չափավոր | Գերազանց |
| Ծախս | $$ | $$$ | $$ | $$$ | $$ |
| Ուժ (Առաձգական) | ~ 485 mpa | ~500 MPa | ~510 MPa | ~520 MPa | ~520 MPa |
| Երկարացում | 40% | ~45% | ~45% | ~45% | ~45% |
| Առողջություն | Excellent for cast parts | Excellent for cast parts | Good for cast parts | Good for cast parts | Գերազանց (for rolled or formed parts) |
| Դիմումներ | Water systems, food-grade parts | Քիմիական, ծովային, օֆշորային | General industrial parts | Ծովային, քիմիական, օֆշորային | High-ductility, Նիհար պատերով մասեր |
11. Եզրափակում
Ամփոփելով, CF3 stainless steel merges the proven corrosion resistance of 304 with the versatility of casting.
Its balanced chemistry, robust mechanical profile, and proven long‑term durability make CF3 an authoritative choice for medium‑duty corrosive environments.
Որեվէ ավելին, with annual global production exceeding 50,000 tonnes and scrap rates under 6 %, CF3 delivers both economic and performance advantages.
Անհամբեր սպասում եմ, integrating CF3 into hybrid casting–additive workflows and exploring surface treatments promises to extend its service envelope—ensuring CF3 remains a cornerstone alloy in industrial applications.
Լանջ Ձեր արտադրության կարիքների համար կատարյալ ընտրություն է, եթե ձեզ հարկավոր է որակյալ Չժանգոտվող պողպատից ձուլում.
FAQs on CF3 Stainless Steel
Is CF3 Stainless Steel suitable for high-temperature applications?
CF3 is generally suitable for moderate-temperature applications (up to about 800°F or 427°C).
For higher temperatures, or when Օքսիդացման դիմադրություն at elevated temperatures is critical,
other grades like Cf8m կամ 316 Չժանգոտվող պողպատ may be more appropriate due to their enhanced high-temperature properties.
Can CF3 be welded?
Այո, CF3 stainless steel is highly զոդելի. Its low carbon content minimizes the risk of carbide formation during welding, reducing the chances of intergranular corrosion.
Այնուամենայնիվ, it is always recommended to use appropriate welding techniques և post-weld heat treatments when working with this material in critical applications.
Is CF3 Suitable for Cryogenic Applications?
Այո, CF3 exhibits good toughness at low temperatures, making it suitable for use in cryogenic applications such as liquefied natural gas (LNG) storage and transportation.
Can CF3 Be Heat Treated?
CF3 is generally not heat treatable for strengthening purposes. Այնուամենայնիվ, it can be annealed to relieve stresses and improve machinability.
How does CF3 Stainless Steel perform in seawater?
CF3 offers moderate resistance to seawater corrosion, but it is not as resistant as CF3M or CF8M, which have enhanced chloride resistance due to the presence of մոլիբդեն.
Մեջ Ծովային միջավայրեր with high salinity, CF3 may experience some Խոռոչի կոռոզիայից ժամանակի ընթացքում, so CF3M or CF8M might be more suitable.
How should CF3 Stainless Steel be maintained?
Regular maintenance of CF3 stainless steel includes:
- Մաքրում: Removing contaminants such as chlorine, աղ աղ, and chemicals that could cause localized corrosion.
- Զննում: Checking for any signs of թաթ կամ Crevice Corrosion, Հատկապես ծովային կամ chemical environments.
- Եռակցում: Ensuring proper զոդում He երմամշակում to avoid cracking or sensitization.
Can CF3 Stainless Steel be used in food contact applications?
Այո, CF3 is often used in Սննդի վերամշակման սարքավորումներ դրա շնորհիվ Կոռոզիոն դիմադրություն և ease of cleaning.
It complies with Fda և 3-A Sanitary Standards, այն դարձնելով հարմար ընտրություն սանիտարական փականներ, պոմպեր, եւ խողովակների համակարգեր.