What Is Case Hardening and How Does It Work?

1. Santrauka

Case hardening creates a thin, very hard surface layer (the “case”) on a tougher, Kario šerdis. It combines surface wear and fatigue resistance with a ductile core that resists shock.

Typical uses are gears, velenai, CAMS, pins and bearings. Achieving excellent functional performance is an engineering task (metalurgija, proceso valdymas, distortion management, tikrinimas).

Making the part look great requires planning: control where and how finishes are produced, sequence polishing/grinding relative to heat treatment, and finish with an appropriate protective and decorative surface treatment (Pvz., controlled temper colors, juodas oksidas, PVD, Lakas).

2. What is case hardening?

Bylos sukietėjimas (Taip pat vadinamas surface hardening) is the family of metallurgical processes that produce a hard, wear-resistant surface layer — the case — on a part while leaving a relatively soft, ductile interior — the šerdis.

The objective is to combine high surface hardness and wear/fatigue resistance su core toughness and impact resistance, delivering components that resist surface damage without becoming brittle through-and-through.

Core concepts

• Kietas paviršius (case): a thin zone (typically tenths of a millimetre to a few millimetres) engineered to be hard (Pvz., 55–64 HRC for carburized martensite or 700–1,200 HV for nitrides).
• Ductile core: the bulk material remains relatively soft and tough to absorb shocks and avoid catastrophic brittle fracture.
• Gradual transition: a controlled hardness gradient from the surface into the core (not an abrupt interface) to improve load transfer and fatigue life.
• Localized treatment: case hardening can be applied to entire parts or selectively to functional zones (bearing journals, gear teeth, contact faces).

3. Common case-hardening processes

Below I describe the principal case-hardening technologies you will encounter in engineering practice.

Carburizacija (dujos, vacuum and pack variants)

Mechanizmas: carbon is diffused into the steel surface at elevated temperature to raise the near-surface carbon content; the part is then quenched to form a martensitic case and tempered to achieve the required combination of hardness and toughness.

Variantai & sąlygos:

• Dujos Carburizacija (industrial standard): performed in a controlled hydrocarbon atmosphere (endothermic gas or natural gas mixtures) at roughly 880–950 ° C..
  Carbon potential and soak time determine case depth; practical effective case depths commonly range from 0.3 mm 2.5 mm for many components; surface hardness after quench/temper typically 58–62 HRC for high-carbon martensite.
• Vakuumas (žemo slėgio) Carburizacija: uses hydrocarbon injection in a vacuum furnace, often at 900–1050 ° C. with subsequent high-pressure gas quench.
  Advantages include minimal oxidation/scale, excellent carbon control and lower residual distortion; this route is favored where surface appearance and tight tolerances are required.
• Pack (kietas) Carburizacija: older shop method using carbonaceous powders at 900–950 ° C.; lower capital cost but poorer control and cleanliness—less suited for appearance-critical parts.

Argumentai: can produce relatively deep, tough martensitic cases; well understood and economical for medium–large production.
Trūkumai: quenching from high temperature causes significant thermal stress and potential distortion; surface oxidation and scaling must be managed (especially in conventional gas or pack carburizing).

Carbonitriding

Mechanizmas: a combined diffusion of carbon and nitrogen into the surface at temperatures generally lower than carburizing, followed by quench and temper.
Nitrogen increases surface hardness and may improve wear and scuff resistance relative to carburized only cases.

Sąlygos: typical process temperatures are 780–880 ° C.; effective case depths are shallower than carburizing, paprastai 0.1–1,0 mm, and surface hardnesses after quench/temper land around 55–60 HRC for appropriate steels.

Argumentai: faster cycles and good as-machined wear properties; produces a tougher, nitrogen-enriched case beneficial for abrasive or adhesive wear.
Trūkumai: shallower case depth limits use under high contact stresses; proceso valdymas (atmosphere purity, ammonia level) is critical to avoid undesirable compound layers or color irregularities.

Nitridavimas (dujos, plasma/ion, and salt bath)

Mechanizmas: nitrogen diffuses into steel at relatively low temperatures to form hard nitrides (Pvz., FeN, Crn, AlN) within a diffusion zone; no quench is required because the process generally occurs below the austenitizing temperature.

The result is a hard, wear-resistant surface with very low distortion.

Variantai & sąlygos:

• Dujos nitridavimas: performed at 480–570 °C in an ammonia-based atmosphere; case depths typically 0.05–0.6 mm (diffusion zone), with surface hardness often in the 700–1,200 HV range depending on steel chemistry and time.
• Plazma (ion) nitridavimas: uses a low-pressure glow discharge to activate nitrogen; offers superior uniformity, better control of the compound (balta) sluoksnis, and a clean surface finish—advantages for aesthetic parts.
  Typical temperatures are 450–550 ° C. with adjustable bias to tune surface finish.
• Salt-bath nitriding / nitrocarburizing (Pvz., Tenifer, Melonite): chemically active baths at ~560–590 °C produce good wear and corrosion characteristics but require careful environmental and waste handling.

Argumentai: minimalus iškraipymas, excellent fatigue and wear performance, improved corrosion resistance in many cases, and attractive, consistent finishes (especially plasma nitriding).
Trūkumai: diffusion layer is relatively thin compared with carburizing; steels must contain nitride-forming elements (Al, Kr, V, Iš) for best results; harmful compound layers (“white layer”) can form if parameters are not controlled.

Indukcijos sukietėjimas

Mechanizmas: high-frequency electromagnetic induction rapidly heats a surface layer to austenitizing temperature; a rapid quench (water or polymer) transforms the heated layer to martensite.
Because heating is local and very fast, hardening can be applied selectively and cycle times are short.

Tipiški parametrai: surface temperatures often in the range 800–1100 ° C. for short times (sekundės), with case depths controlled by frequency and time—from 0.2 mm up to several millimetres. Surface hardness commonly 50–65 HRC depending on steel and quench.

Argumentai: highly localized hardening (guoliai, gear flanks, journals), very high throughput, reduced cycle energy, and reduced overall distortion relative to full-part quench if properly fixtured.
Trūkumai: requires geometry amenable to induction coils; edge overheating or flash can produce discoloration; limitations on minimum wall thickness and effective hardenability of the chosen steel.

Flame hardening

Mechanizmas: surface heating by oxy-fuel flame to austenitizing temperature followed by quench.
A relatively simple field-repair capable technique that mimics induction hardening but uses flame as the heat source.

Typical conditions: surface heating to ~800–1000 °C immediately followed by quenching; case depths often 0.5–4 mm depending on heat input and quench.

Argumentai: flexible for large or field repairs, low capital equipment needs.
Trūkumai: less uniform heat application than induction; higher risk of scale, oxidation and visual discoloration; greater skill required to achieve consistent aesthetic results.

Ferritic nitrocarburizing and low-temperature thermochemical processes

Mechanizmas: low-temperature surface enrichment of nitrogen and carbon while the steel is in the ferritic state (below A1), producing a hard compound layer and diffusion zone without transforming the bulk microstructure.

Typical systems: salt bath ferritic nitrocarburizing or gas variants at ~560–590 °C produce shallow hard layers with improved wear and corrosion resistance and low distortion.

Argumentai: Puikus matmenų stabilumas, improved corrosion resistance and a characteristic dark matte finish that is useful for appearance.
Trūkumai: environmental concerns with certain salt baths (choose environmentally compliant processes) and limited case depth.

Thin hard coatings (PVD, CVD, DLC) — not diffusion cases but often used with case hardening

Mechanizmas: physical or chemical vapor deposition deposits a very thin, extremely hard layer (Alavas, Crn, Ticn, DLC) onto a substrate.
These are not diffusion cases; they rely on adhesion and thin-film mechanics rather than a graded metallurgical transition.

Typical attributes: coating thickness typically a few micrometres; hardness in the thousands of HV; visually striking (gold TiN, black DLC) and excellent wear/tribological performance.

Argumentai: excellent decorative finishes and additional wear resistance; compatible with nitrided substrates for improved adhesion and fatigue behavior.
Trūkumai: coatings are thin—do not replace the need for a diffusion case where contact fatigue or deep wear resistance is required—adhesion depends on surface prep and substrate condition.

4. Material suitability and selection

5. Key Strategies to Optimize the Appearance of Case-Hardened Surfaces

Achieving a “great look” requires a systematic approach that integrates pre-treatment preparation, process parameter control, post-treatment finishing, ir defect prevention.

Each step directly impacts surface aesthetics and functional performance.

Pre-Treatment: The Foundation of Aesthetic Uniformity

Paviršiaus teršalai (aliejus, tepalas, rūdis, skalė) and material defects (poringumas, įbrėžimai) are amplified during case hardening, leading to uneven color, mastelio keitimas, or coating failure.
Pre-treatment steps must ensure a clean, uniform surface:

• Degreasing and Cleaning: Use ultrasonic cleaning (with alkaline detergents) or vapor degreasing (with trichloroethylene) to remove oil and grease.
  Avoid chemical cleaners that leave residues (Pvz., chloride-based solutions), which cause pitting during heat treatment.
  According to ASTM A380, the surface must have a water-break-free finish (no beading) after cleaning.
• Šlifavimas ir poliravimas: For aesthetic-critical parts, Tikslus šlifavimas (surface roughness Ra ≤ 0.8 μm) ir poliravimas (Ra ≤ 0.2 μm) remove scratches, įrankių žymės, ir paviršiaus nelygumai.
  This ensures uniform heat absorption and diffusion during case hardening, preventing localized discoloration.
• Shot Blasting/Pickling: Šūvys sprogdinimas (with glass beads or aluminum oxide) removes rust and scale, improving surface adhesion for post-treatment.
  Marinavimas (with dilute hydrochloric acid) is used for heavy scaling but must be followed by neutralization to avoid surface etching.

Post-Treatment Finishing: Enhancing Aesthetics and Functionality

Post-treatment transforms the as-hardened surface into a visually appealing finish while preserving or enhancing functional properties (dėvėti, atsparumas korozijai).

The choice of finishing method depends on the base process, medžiaga, ir estetiniai reikalavimai:

Mechanical Finishing

• Poliravimas: For carburized or induction-hardened parts, sequential polishing (coarse to fine abrasives: 120 grit → 400 grit → 800 smilkė) achieves a mirror finish (Ra ≤ 0.05 μm).
  Use diamond abrasives for hard surfaces (HRC ≥ 60) to avoid scratching. Polishing after nitriding enhances the golden-brown color and improves corrosion resistance.
• Buringimas: Use a cotton or felt wheel with polishing compounds (aliuminio oksidas, Chromo oksidas) to create a glossy finish.
  Buffing is ideal for decorative parts (Pvz., Automobilių apdaila, jewelry fasteners) but may reduce surface hardness slightly (by 2–5 HRC).
• Nušauti peening: For non-glossy, matte finishes, shot peening with fine glass beads (0.1–0,3 mm) creates a uniform texture while improving fatigue strength. The surface roughness can be controlled between Ra 0.4–1.6 μm.

Chemical and Electrochemical Finishing

• Juodojo oksido danga: Also known as bluing, this process forms a thin (0.5– 1,5 μm) black iron oxide (Fe₃o₄) film on the surface. It is compatible with carburized and nitrided parts, providing a uniform black finish with mild corrosion resistance.
  The process (ASTM D1654) uses a hot alkaline solution (135–145℃) and requires post-oiling to enhance aesthetics and corrosion protection.
• Elektropliacija: Chromo danga (kietas chromas, decorative chrome) or nickel plating can be applied after case hardening to create a glossy, Atsparus korozijai.
  Ensure the surface is free of scale and porosity (via pre-polishing) to avoid plating defects (bubbling, peeling). Decorative chrome plating achieves a mirror finish with a Vickers hardness of 800–1000 HV.
• Cheminės konversijos dangos: Fosfation (zinc phosphate, manganese phosphate) forms a gray or black crystalline film that improves paint adhesion.
  It is used for parts requiring both aesthetics and corrosion resistance (Pvz., Mašinų komponentai).
  Anodizing is suitable for stainless steel nitrided parts, producing a range of colors (mėlyna, juodas, auksas) via electrolytic oxidation.

Coating Technologies for Advanced Aesthetics

• Fizinis garų nusėdimas (PVD): PVD dangos (Alavas, Ticn, Crn) are applied via vacuum deposition, producing thin (2–5 μm), Sunku, and visually consistent films.
  TiN offers a golden finish (popular in cutting tools and luxury hardware), while CrN provides a silver-gray finish. PVD is compatible with nitrided parts and enhances both aesthetics and wear resistance.

  

• Cheminis garų nusėdimas (CVD): CVD coatings (Į deimantą panaši anglis, DLC) create a matte black or glossy finish with exceptional hardness (HV ≥ 2000) ir atsparumas korozijai.
  They are ideal for high-performance parts (Pvz., aviacijos ir kosmoso komponentai) but require high-temperature processing (700–1000℃), which may affect the core properties of case-hardened parts.

6. Bendri trūkumai, root causes, and prevention

7. Aesthetic design considerations for case-hardened components

A visually successful case-hardened part is the product of integrated design, process selection and finishing — not an afterthought.

Specify process consistency for color matching

If parts are intended to be seen together (gear sets, fastener kits, assemblies), require the same hardening and post-treatment route across the set.

Plasma nitriding followed by a given post-finish (juodas oksidas, clear lacquer or PVD) produces highly repeatable tones;

mixing fundamentally different processes (for example carburizing on one part and nitriding on another) makes consistent color and surface response difficult to achieve and should be avoided when visual uniformity is required.

Use deliberate texture contrast to create visual hierarchy

Combine matte and polished zones to emphasize form and function.

Pavyzdžiui, a polished nitrided tooth flank contrasted with a shot-peened or bead-blasted hub creates an attractive, engineered look while serving functional needs (polished teeth reduce friction; matte hubs improve grip and hide handling marks).

Define texture targets quantitatively (Ra or surface finish class) so finishers can reproduce the effect.

Design geometry to control thermal effects and dimensional stability

Geometry influences heating, cooling and distortion during surface hardening. Add generous fillets, avoid sharp abrupt section changes, and balance cross-sectional mass to reduce the risk of edge overheating and warpage.

For induction hardening, observe practical minimum section rules (typical minimum wall/thickness ≈ 3 mm) and allow for fixturing to ensure uniform heating.

Where tight post-hardening tolerances are required, plan for rough machining before treatment and finish grinding afterward.

Integrate corrosion-protection into the aesthetic plan

Lauke, marine or exposed architectural use, combine the case hardening route with durable corrosion finishes that preserve color over time.
Pavyzdžiai: plasma-nitrided stainless steel followed by a clear DLC or PVD topcoat for long-term color stability; carburized housings that receive electroless nickel or powder coating on non-sliding areas.
Specify compatible coating systems and curing/pretreatment steps (nuriebalinti, Passvate, fosfatas) to avoid adhesion problems and maintain appearance.

Protect functional surfaces and plan masking/assembly

Decide early which surfaces must retain the diffusion case (bearing journals, sandarinimo veidai) and which may receive decorative coatings.
Use masking or removable inserts during finishing when coatings would impair function.

Where mating surfaces must remain uncoated, document this in drawings and process sheets to avoid accidental coverage.

Tolerancing and finish sequence control

Document the finish sequence: rough machine → harden → finish grind/polish → final coating. State dimensional tolerances after hardening if no post-grind is planned.
For aesthetic quality, define acceptance criteria (color reference, gloss or matte target, allowable blemishes) and require photographic or sample approvals on first articles.

8. Application-Specific Aesthetic Optimization Examples

The following examples illustrate how to tailor case hardening and finishing for different industries, balancing aesthetics and functionality:

Automobilių komponentai (Pavaros, Velenai, Apdaila)

For transmission gears (20MnCr5 steel): Gas carburizing (case depth 1.0 mm) → quenching + tempering → precision grinding (Ra 0.4 μm) → black oxide coating. This achieves a uniform black finish with high wear resistance.

For luxury automobilių apdaila (4140 plienas): Plazmos nitridavimas (golden-brown finish) → buffing → clear PVD coating. The clear coating preserves the golden color and enhances corrosion resistance.

Precision Tools (Pjovimo įrankiai, Wrenches)

For cutting tools (HSS steel): Nitridavimas (case depth 0.2 mm) → TiN PVD coating. The golden TiN finish is visually distinctive and provides exceptional wear resistance.

For wrenches (1045 plienas): Induction hardening → shot peening (matinis apdaila) → manganese phosphating. The gray phosphate finish improves grip and prevents rust.

Architectural Hardware (Door Handles, Railings)

For stainless steel door handles (316 plienas): Plasma nitriding → anodizing (black or bronze) → clear coat. The anodized finish offers color customization and weather resistance.

For cast iron railings: Flame hardening → sandblasting (matte texture) → powder coating. Powder coating provides a durable, uniform finish in a range of colors.

9. Tvarumas, safety and cost considerations

• Energija & išmetamųjų teršalų kiekis: heat treating is energy-intensive. Vacuum carburizing reduces emissions from combustion but uses electricity and gas pulses. Optimize cycle times and load density to reduce footprint.
• Aplinka & saugumas: avoid legacy cyanide or hexavalent chromium salts. Prefer vacuum, dujos, plasma or environmentally controlled salt baths with approved waste handling.
• Kainos vairuotojai: Proceso pasirinkimas (vacuum vs gas vs induction), ciklo laikas, secondary grinding and finishing, scrapping rates due to distortion.
  Choose process matched to required performance: vacuum carburize for precision, nitriding for low distortion, induction for low volume localized hardening.
• Gyvenimo ciklas & remontas: nitrided and PVD finishes extend life with low rework; induction hardening enables field re-hardening in some cases.

10. Išvada

Case hardening is a versatile surface modification technology that, when optimized, can deliver both superior functional performance and exceptional aesthetics.

The key to a “great look” lies in systematic process control (išankstinis gydymas, parameter optimization, post-finishing) ir application-specific tailoring (Medžiagos pasirinkimas, defect prevention, design integration).

Chemical processes like plasma nitriding offer inherent aesthetic advantages (uniform color, minimal deformation), while thermal processes like induction hardening require more post-treatment to achieve visual appeal.

Advanced finishing technologies (PVD, DLC coatings) bridge the gap between functionality and aesthetics, enabling case-hardened parts to meet the demands of high-end applications.

 

DUK

What is the difference between case depth and case hardness?

Case depth is the thickness of the hardened/diffused layer; case hardness is the hardness at or near the surface.

Both must be specified because a thin very-hard case may fail rapidly, while a deep but soft case may not resist wear.

Should I polish before or after case hardening?

Critical functional surfaces (bearing journals, sandarinimo veidai) should be finish-ground po grūdinimas. Pre-hardening polishing is acceptable only for decorative surfaces that won’t be ground later.

How deep should the case be for gears?

Typical gear faces are carburized to 0.6–1,5 mm effective case depth (depth to a defined hardness) depending on load. Heavy-duty gears may require deeper cases or through-hardening alternatives.

Is nitriding “better” than carburizing?

It depends. Nitriding gives very low distortion, excellent surface hardness, and better corrosion resistance in some environments, but the case is thinner and nitrided surfaces lack the martensitic core toughness obtainable by carburizing + gesinimas. Choose by application.

How to avoid cracking after case hardening?

Control material chemistry, use proper preheat and quench practice, use appropriate temper cycles and reduce retained austenite (subzero if necessary).

Avoid hard, brittle untempered microstructures on thin sections.

Can PVD be applied over a carburized surface?

Yes — but surface preparation (valymas, possibly thin diffusion barrier) and control of deposition parameters are required for adhesion.

PVD layers are thin and primarily decorative/wear-enhancing, not a substitute for a diffusion case.