1. Ներածություն
CD4MCU (commonly supplied to cast-steel specifications such as ASTM A890 Grade 1A for duplex castings with UNS number J93370) is a purpose-engineered duplex stainless casting that combines high strength, elevated resistance to localized corrosion, and good erosion/cavitation resistance.
Its chemistry (high chromium, մոլիբդեն, copper and nitrogen with moderate nickel) and two-phase (ֆերիտ + Օստենիտ) microstructure make CD4MCu a popular choice for demanding wet-service rotating components (Տեղադրում, պոմպի պատյաններ), փականներ, and other cast hardware where chloride exposure, erosion or mechanical load are present.
2. What is CD4MCu Stainless Steel?
CD4MCu is a կրկնակի (Ferritic-austenitic) Չժանգոտվող պողպատ grade provided principally in cast product forms.
It is formulated to give a balanced duplex microstructure (≈ 35–55% ferrite typical in well-processed castings) that yields high yield strength, good toughness and significantly improved resistance to pitting, crevice corrosion and chloride stress-corrosion cracking relative to conventional austenitic cast grades (օր., CF8M/316 cast).
The “Cu” in the designation reflects a deliberate copper addition (≈ 2.7–3.3 wt%) that enhances resistance to certain reducing and erosive chemistries and improves performance in cavitating or slurry environments.
Հատկություններ
- Բարձր մեխանիկական ուժ (yield substantially higher than CF8M/316 castings).
- Elevated localized-corrosion resistance (Mo and N boost PREN; copper improves behavior in some reducing chemistries).
- Good erosion/cavitation resistance for rotating wet components.
- Ամրություն բարդ երկրաչափությունների համար (Տեղադրում, պտտվում են, Փական մարմիններ).
- Լավ զոդում when qualified procedures and matching fillers are used.
- Balanced duplex microstructure provides damage-tolerant toughness while increasing fatigue resistance vs many austenitics.
3. Typical Chemical Composition of CD4MCu Stainless Steel
| Տարր | Բնորոշ տիրույթ (Wt.%) | Դեր / comment |
| Գ | ≤ 0.04 | Keep low to avoid carbide precipitation |
| Խուզարկու | 24.5 Մի քիչ 26.5 | Primary passive-film former; key to general corrosion resistance |
| Մեջ | 4.5 Մի քիչ 6.5 | Austenite former; helps duplex balance |
| Ժամանակ | 1.7 Մի քիչ 2.5 | Strengthens pitting/crevice resistance |
Մգոհել |
2.7 Մի քիչ 3.3 | Improves resistance to reducing acids, cavitation/erosion behavior |
| Ն | 0.15 Մի քիչ 0.25 | Strengthener and powerful PREN booster |
| Ժլատ | ≤ 1.0 | Deoxidizer/processing aid |
| Մի քանազոր | ≤ 1.0 | Deoxidation and oxidation resistance |
| Իմաստ | ≤ 0.04 | Կեղտաջրերի վերահսկում |
| Ծուռ | ≤ 0.03 | Low S for soundness |
| Անք | Հավասարակշռություն | Matrix տարր (ֆերիտ + Օստենիտ) |
4. Mechanical Properties — CD4MCu (ASTM A890 դասարան 1 ա)
Ստորև ներկայացված է կենտրոնացված, engineering-grade presentation of the typical mechanical behaviour of CD4MCu in the usual supply condition (դարակ, Լուծում-օծանելիք, ջրմուղ- or air-quenched as specified by the foundry).
Սենյակ-ջերմաստիճան (բնորոշ) mechanical properties — solution-annealed cast CD4MCu
| Սեփականություն | Բնորոշ տիրույթ (Մի քանազոր) | Բնորոշ տիրույթ (imperial) | Մեկնաբանություն |
| Առաձգական ուժ, Ժլատ | 650 Մի քիչ 780 MPA | 94 Մի քիչ 113 ksi | Dependent on section size and foundry practice; heavier sections trend lower. |
| 0.2% ապացույց / Զիջել, RP0.2 | 450 Մի քիչ 550 MPA | 65 Մի քիչ 80 ksi | Use heat-specific value for allowable stress calculations. |
| Երկարացում, Էունք (%) | 15 Մի քիչ 25 % | Մի քիչ | Measured on standard test specimens; decreases with heavier sections and casting defects. |
| Reduction of area, Z (%) | 30 Մի քիչ 40 % (բնորոշ) | Մի քիչ | Indicative of ductile fracture when casting quality is high. |
Բրինելի կարծրություն (Ժխտել) |
220 Մի քիչ 280 Ժապավենի | ≈ 85 Մի քիչ 110 Ժլատ | Higher hardness correlates with higher strength but may signal microstructural issues if above expected. |
| Առաձգականության մոդուլ, Եփ | ≈ 190 Մի քիչ 205 Gpa | ≈ 27.6 Մի քիչ 29.7 ×10³ ksi | Use ~200 GPa for stiffness calculations unless supplier data differ. |
| Խարխլված v-notch, CVN (սենյակ Թ) | Սովորաբար լավ; specify if fracture-critical (օր., ≥ 20–40 J target) | Մի քիչ | CVN is heat- and section-dependent; require supplier test if toughness is critical. |
| Հոգնածություն (ուղղորդում) | Endurance (smooth specimen) ≈ 0.30–0.45 × Rm | Մի քիչ | Strongly dependent on surface finish, Ձուլման թերություններ, residual stresses and detail geometry. Component testing recommended. |
5. Physical and Thermal Properties of CD4MCu Stainless Steel
| Սեփականություն | Representative value |
| Խտություն | ≈ 7.80 Մի քիչ 7.90 g · cm⁻³ |
| Mal երմային հաղորդունակություն (20 ° C) | ≈ 12 Մի քիչ 16 W·m⁻1·K-1 |
| Specific heat (20 ° C) | ≈ 430 Մի քիչ 500 J·kg-1·K-1 |
| Ջերմային ընդարձակման գործակիցը (20-100 ° C) | ≈ 12.0 Մի քիչ 13.5 × 10⁻⁶ k⁻¹ |
| Առաձգականության մոդուլ (Եփ) | ≈ 190 Մի քիչ 205 Gpa |
| Melting/solidus (Մոտավոր:) | ~1375 – 1450 ° C (համաձայրած) |
6. Կոռոզիայի ներկայացում
- Թաթ & ճեղքվածք: CD4MCu’s Mo + Ն + high Cr give strong resistance; PREN in the low-30s makes it suitable for brackish water, many cooling-water systems and chloride-containing process streams at moderate temperatures.
- Շալվար (chloride stress-corrosion cracking): duplex microstructure and lower austenite fraction confer greater resistance to chloride SCC than typical austenitic cast grades;
սակայն, SCC can still occur under severe combinations of chloride, temperature and tensile stress. - Էրոզիա-կոռոզիա / սրընթացություն: copper addition and high strength improve resistance to erosion-assisted corrosion and cavitation pitting; this is why CD4MCu is used for impellers and slurry pumps.
- Reducing acids: CD4MCu is more tolerant than 316 in some mildly reducing fluids, but concentrated hot reducing acids may require higher-alloy or nickel-base materials.
- Ջերմաստիճանի սահմանները: for long-term chloride service prefer exposures at or below levels validated by lab screening; at elevated temperatures generalized corrosion rates and localized attack susceptibilities increase.
7. Casting Characteristics of CD4MCu Stainless Steel
CD4MCu is typically delivered as ներդրում կամ sand cast Բաղադրիչներ.
Key casting considerations:
- Solidification and shrinkage: expect typical linear shrinkage in the order of ~1.2–2.0% — use foundry shrink factors for pattern design. Directional solidification and properly placed risers avoid shrink cavities.
- Melt control: controlled induction melting, argon degassing and ceramic filtration reduce gas and inclusions; vacuum melting or ESR may be used for the highest integrity castings.
- Common casting defects: Գազի ծակոտկենություն, Նեղացման խոռոչներ, non-metallic inclusions and cold shuts — prevented by correct gating, ֆիլտրում, degassing and pour control.
- Post-cast heat treatment: Լուծում Անալի (see section 8) is needed to attain the desired duplex balance and dissolve segregated phases. Հիփ (hot-isostatic pressing) can be used for critical, high-integrity parts to close internal porosity.
- Վերամբարձ allowances & հանդուրժողականություններ: provide realistic machining stock (օր., 2–6 mm roughing allowance; less for investment castings) and specify machined critical faces.
8. Կեղծում, He երմամշակում, and Welding Best Practices
He երմամշակում
- Լուծում Անալի after casting (typical temperature range around 1040–1100 °C; exact foundry specification to be followed) with rapid quench to lock in balanced duplex microstructure and dissolve undesirable precipitates.
Some sources advise a heat treatment around ~1900 °F (~1038 °C) followed by quench for cast duplex grades; follow supplier/foundry datasheet for exact temp/hold/quench.
Եռակցում
- Weldability is good, but control is essential: use qualified welding procedures (WPS/WPQ), matching filler metals designed for duplex chemistry, control interpass temperature, and limit heat input to maintain phase balance in HAZ.
- Post-weld solution anneal: not always practicable for completed assemblies; if not possible, select appropriate filler alloys and minimize HAZ extent to preserve local corrosion resistance.
Վերամբարձ & ձևավորելով
- Machinability of CD4MCu is moderate; use carbide tooling, appropriate feeds and coolant.
Duplex grades are stronger than austenitics so expect higher tool wear. Cold forming is limited compared with ductile austenitics; design drawings accordingly.
Մակերեւույթի պատրաստում & պասիվություն
- After welding/repair remove heat tint and pickle as required, and then passivate with nitric or citric passivation processes to restore a uniform passive film.
9. Industrial Applications of CD4MCu (ASTM A890 դասարան 1 ա)
CD4MCu is widely used where cast geometry, elevated strength and improved localized-corrosion/erosion resistance are required:
- Պոմպի բաղադրիչները: Տեղադրում, volutes and casings for seawater, խնձոր ջուր, cooling water and slurry services.
- Փական մարմիններ & զարդարել: control and isolation valves in offshore, անկարգություն, քիմիական, and power plant systems.
- Անկարգություն & reverse-osmosis equipment: rotating hardware and fittings exposed to chlorides and transient conditions.
- Պղտոր & paper and mining equipment: slurry pumps and wear-prone components.
- Քիմիական գործընթաց & Սառեցման համակարգեր: where chloride levels and mechanical load combine.
10. Առավելությունները & Սահմանափակումներ
Core Advantages of CD4MCu (ASTM A890 դասարան 1 ա)
- Հավասարակշռված ուժ եւ կոռոզիոն դիմադրություն: Yield strength twice that of 316L with comparable or superior corrosion resistance in chloride and acid media.
- Superior sour service performance: Complies with NACE MR0175, making it ideal for H₂S-containing environments.
- Գերազանց կուտելիություն: Suitable for complex-shaped components that are difficult to fabricate via wrought processes.
- Ծախսարդյունավետություն: 30–50% cheaper than nickel-based alloys (օր., Hastelloy c276) while offering similar corrosion resistance in moderate environments.
- Հագուստի դիմադրություն: Copper addition enhances resistance to abrasion and erosion, extending service life in fluid-handling applications.
Key Limitations of CD4MCu (ASTM A890 դասարան 1 ա)
- Welding complexity: Requires strict heat input control and mandatory PWHT, increasing fabrication costs compared to austenitic steels.
- Temperature restriction: Not suitable for continuous service above 450°C due to σ phase formation.
- Sensitivity to residual elements: Բարձր մնային (>0.8%) or Sn/Pb impurities reduce corrosion resistance and increase cracking risk.
- Lower ductility than austenitic steels: Երկարացում (16–24%) is lower than 316L (≥40%), limiting use in high-deformation applications.
11. Comparative analysis — CD4MCU versus similar alloys
Values are representative, for screening and specification drafting only — always use supplier MTRs, manufacturer datasheets and application-specific test data for final selection.
| Ասպեկտ / Խառնուրդ | CD4MCU (ձուլված դուպլեքս) | Cf8m / Դարակ 316 (օստենիտիկ) | Կրկնակի 2205 (կռիվ) | Nickel-base (օր., C-276) |
| Composition highlights | Cr ~24.5–26.5; Ni ~4.5–6.5; Mo ~1.7–2.5; Cu ~2.7–3.3; N ~0.15–0.25 | Cr ~16–18; Ni ~10–14; Mo ~2–3 (Cf8m) | Cr ~21–23; Ni ~4–6.5; Mo ~3; N ~0.08–0.20 | Very high Ni and Cr; substantial Mo (and other alloying) |
| Typical PREN (screening) | 30-35 (depends on Mo/N) | ~24–27 | 35-40 | >40 (տատանվում է համաձուլվածքով) |
| Representative mechanical (Ժլատ / RP0.2) | Rm 650–780 MPa; Rp0.2 450–550 MPa | Rm ≈ 480–620 MPa; Rp0.2 ≈ 170–300 MPa | Rm ≈ 620–880 MPa; Rp0.2 ≈ 400–520 MPa | Rm variable (often 500–900 MPa); Rp0.2 depends on grade |
| Chloride SCC resistance | Լավ (better than CF8M; duplex benefit) | Moderate — susceptible under hot/stressed conditions | Շատ լավ (one of best stainless choices for SCC) | Ընդհանուր առմամբ գերազանց (engineered for extreme chemistries) |
Թաթ / Crevice դիմադրություն |
Բարձր (Ժամանակ + Ն + Խուզարկու; PREN ~30s) | Չափավոր | Շատ բարձր | Գերազանց |
| Քայքայում / Կավագործության դիմադրություն | Լավ (Մգոհել + higher strength improve performance) | Չափավոր | Լավ (higher strength helps) | Variable — depends on grade; often chosen for corrosion rather than erosion |
| Ամրություն / product forms | Excellent as castings (Տեղադրում, պտտվում են, Փական մարմիններ) | Գերազանց (cast forms widely available) | Հիմնականում կռիվ (ափսե, բարերար, խողովակ); some cast duplex exists but more complex | Wrought and cast; castings possible but costly |
| Եռակցման հնարավորություն & HAZ behavior | Good — requires qualified procedures and HAZ control | Գերազանց (316 is forgiving) | Weldable but requires strict control to preserve duplex balance | Weldable with qualified procedures; filler choice critical |
| Typical cost band (նյութական) | Mid–high (less than most Ni alloys) | Իջնել (տնտեսական) | Mid–high (similar to CD4MCu or higher for high-spec) | Բարձր (premium alloys) |
Բնորոշ ծրագրեր |
Տեղադրում, պոմպի պատյաններ, valve bodies for brackish/seawater, Խիտ պոմպեր, անկարգություն, cooling water | General process piping, տանկ, sanitary equipment, moderate chloride service | Օֆշորային, անկարգություն, high-strength chloride services, pressure systems | Քիմիական ռեակտորներ, extreme acid/chloride service, very high corrosion severity |
| Երբ ընտրել | Need complex cast parts with high strength, good pitting/SCC and erosion resistance at moderate cost | Cost-driven projects where chloride exposure is low–moderate and fabrication simplicity is desired | When highest chloride resistance and strength required and wrought form is acceptable | When service chemistry or temperature exceeds stainless/duplex capability and life-cycle cost justifies premium |
12. Եզրափակում
CD4MCU (ASTM A890 Grade 1A when specified in cast duplex form) is a technically attractive option for rotating and pressure-containing cast components in chloride-bearing, erosive or cavitating services.
Դրա դուպլեքս կառուցվածքը, molybdenum and nitrogen content yield robust pitting resistance and SCC tolerance while copper and high strength enhance resistance to erosion and mechanical damage.
To realize the alloy’s advantages, disciplined foundry practice, documented solution anneal, qualified welding and appropriate NDE are essential.
Where service chemistry or temperature exceeds CD4MCu capability, duplex wrought grades or nickel-base alloys should be evaluated.
ՀՏՀ
What does “CD4MCu” mean?
It denotes a duplex stainless casting grade with composition features (Խուզարկու, Ժամանակ, Cu and N) tuned for improved pitting, SCC and erosion resistance. It is commonly supplied as ASTM A890 Grade 1A in cast duplex specifications.
What is the difference between CD4MCu and 2205 Duplex չժանգոտվող պողպատ?
CD4MCu is a դարակ duplex alloy optimized for complex component fabrication, with copper addition to enhance reducing acid resistance.
2205 է կռիվ duplex alloy with higher nitrogen content (0.14–0.20 wt.%) for austenite stabilization.
While both have similar PREN values (~ 34), CD4MCu is preferred for castings, և 2205 is used for wrought products (ափսեներ, խողովակներ).
Is CD4MCu suitable for seawater?
Yes — CD4MCu is widely used for seawater, brackish water and cooling-water applications; սակայն, specify lab screening and corrosion allowances for long-term immersed or splash-zone service.
Can CD4MCu be welded in the field?
Yes — but welding requires qualified procedures, matching duplex filler metals, controlled heat input and post-weld cleaning/passivation. For critical assemblies consider pre-qualification and welded coupon tests.
How does CD4MCu compare to 316 ձուլում?
CD4MCu offers higher strength and significantly better localized-corrosion and SCC resistance than CF8M/316 castings — enabling longer life in chloride-bearing, erosive environments.